Customization: | Available |
---|---|
After-sales Service: | We Provide All Solutions |
Warranty: | 3years |
Still deciding? Get samples of US$ 1/Square Meter
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment Methods: |
|
---|---|
Support payments in USD |
Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
performance parameter
1. Good transparency
Transparency can reach more than 91%, good texture, suitable for products requiring high transparency.
2. Excellent impact resistance and rigidity
The material is hard and durable, even at low temperature -40°C physical property is also good; Suitable for high impact strength applications.
3. Excellent processability
It can be used in sawing, die-cutting, drilling and laser cutting, cold bending and hot bending, sticking, welding and polishing, printing and painting, and cold bending without whitening, the appearance is beautiful.
4. Good thermal molding
Without preheating can be formed, high precision, shrinkage rate of 2%-3%; Good deep forming, no cracking and uniform thickness.
5. The environmental protection
Recycling does not pollute the environment.
6. Excellent food hygiene
The material is PETG, complies with all major food regulations, such as FDA or BGA, suitable for food container packaging and other purposes. Good oil resistance and chemical resistance to acid, alkali, oil and other corrosion.
7. Low combustion
Good fire resistance, non - combustion - supporting, low smoke emission, no harm after combustion.
performance | condition | international standard | monad | 2mm | 3mm | 6mm |
density | 23ºC | 1183 | kg/m3 | 1270 | 1270 | 1270 |
water-absorbing quality |
23 ° C immersed in water for 24 hours |
62 | % | 0.3 | 0.2 | 0.1 |
Resistance to tensile stress |
50mm/min | 527 | mpa | 53 | 53 | 53 |
tensile stress at break | 50mm/min | 527 | mpa | 31 | 26 | |
Layer v extension |
50mm/min | 527 | mpa | 4.6 | 4.9 | |
Elongation at rupture | 50mm/min | 527 | 230 | 50 | ||
The modulus of elasticity in tension is 23 ° C | 1.0mm/min | 527 | mpa | 2100 | 2200 | 2100 |
The modulus of deflection is 23 ° C | 1.7mm/min | 178 | mpa | 2200 | 2100 | 2000 |
The flexural strength is 23 ° C | 1.7mm/min | 178 | mpa | 60 | 69 | 77 |
Rockwell hardness | 104 | 115 | 117 | |||
Deformation temperature | 0.45Mpa | 75 | 0ºC | R scale | >80 | >85 |
Deformation temperature | 1.80Mpa | 75 | 0ºC | >76 | >80 | |
Light transmittance | mirror surface | % | 87 | 86 | 82 | |
Light transmittance | reflect | % | 88 | 88 | 84 |